 Chlor-Alkali Products
Chlor-Alkali products are basic raw materials for many chemical industries. Main applications are for water treatment and the manufacture of sodium glutamate, synthetic fibers, soap, detergents, dye-stuffs, pulp and paper, leather, pesticides, mineral refining‧‧‧etc.
|
 |
 NaOH Products
| Appearance |
Colorless Liquid |
| NaOH Content |
45 ± 0.5% |
| NaCl |
Below 200ppm |
| Na2CO3 |
Below 2% |
| Na2SO4 |
Below 200ppm |
|
|
HCl Products
| Appearance |
Colorless Liquid |
| HCl Content |
32 ± 0.5% |
| Na2SO4 |
Below 200ppm |
|
|
Hypo Products
| Appearance |
Colorless Liquid |
| NaOCl Content |
12 ± 0.5% |
| NaOH Residual |
1 ± 0.2% |
|
|
PVC Resins
PVC Resins Properties
|
| Grade |
H-61 |
H-66 |
H-73 |
Test Method |
| K-value |
59-62 |
65-67 |
72-74 |
ISO 1628-2 |
| Degree of Polymerization |
800±50 |
1000±50 |
1350±50 |
|
| Apparent Density(g/cc) |
0.52~0.59 |
0.48~0.56 |
0.45~0.53 |
ISO 60 |
Particle Size
(45mesh pass %) |
≧99 |
≧99 |
≧99 |
Honeywell SRA-150 |
| Volatile(%) |
≦0.3 |
≦0.3 |
≦0.3 |
ISO 1269 |
| Foreign Material(grains/100g) |
≦40 |
≦40 |
≦40 |
Visual inspection |
| Residual VCM(ppm) |
<1 |
<1 |
<1 |
ISO 6401 |
|
|
Applications
|
| Grade |
Applications |
| H-61 |
Injection Molding (Pipe Fitting), Hollow-vacuum Forming (Bottle Blowing), Rigid Film, Shrinkable Film. |
| H-66 |
Flexible and Semi-rigid Product For General Purpose (PVC Film, Sheet, Beach Chair, Venetian Blind, Rigid Pipe, Hose, Low Temperature Wire and Cable Insulation. |
| H-73 |
High Impact Flexible Product (PVC leather, Film, Furniture, Shoes), High Impact Sheet, High Voltage Wire and Cable Insulation. |
|
|
Compound Products
|
 |
Compound Products Coding
| PHR And Transparency |
Classification |
A. Rigid, Opaque
B. Rigid, Translucent
C. Rigid, Transparent
D. Semi-Rigid Opaque
E. Semi-rigid, Translucent
F. Semi-rigid, Translucent
G. Soft, Opaque
H. Soft, Translucent
J. Soft, Transparent
X. Others |
A. General Extrusion
B. General Injection
C. Bottle Blowing
D. Packing Bar For Electronic Parts
E. Tubes For Pens
F. Pipettes
G. Heat Shrinkable Film
H. Beach Chairs
J. Wire For Telephone
K. Rigid Pipe For Furniture
L. Profile Extrusion
M. Wire Inner Insulation(60℃)
N. Wire Inner Insulation(75℃)
P. Wire Inner Insulation(90℃)
Q. Wire Inner Insulation(105℃)
R. Wire Inner Insulation(Non-Migration)
S. Wire Outer Insulation
T. Telephone Sets
U. Christmas Light Plugs
V. Shoe Soles (Non-Foaming)
W. Shoe Soles (Foaming)
X. Others
Y. Toys (Air Blowing Nipples)
Z. Plugs：
1. Injection Moulded Fittings
2. Woven Fabrics
3. Air Blowing Nipples |
|
|
SOFT TYPE COMPOUNDS Physical Properties
Extrusion (General Purpose, Beach Chairs, Woven Fabrics)
|
| Grade/Plasticizer Content(PHR) |
SO-30X |
| A |
B |
C |
D |
E |
F |
| Items / Test Method (ASTM) |
30 |
40 |
50 |
75 |
105 |
125 |
| Specific Gravity |
D-792 |
1.31 |
1.27 |
1.26 |
1.20 |
1.16 |
1.14 |
| Hardness (shore A) |
D-2240 |
95 |
90 |
87 |
68 |
50 |
45 |
| Tensile Strength (kg/cm2) |
D-638 |
270 |
210 |
200 |
110 |
80 |
68 |
| Elongation (%) |
D-638 |
240 |
280 |
290 |
345 |
360 |
380 |
| 100% Modulus (kg/cm2) |
D-638 |
220 |
140 |
120 |
60 |
35 |
30 |
| Heating Volatility (%) |
D-1203 |
0.2 |
0.3 |
0.3 |
0.4 |
0.6 |
0.7 |
|
|
|
Injection (General Purpose, Shoe Soles, Sandals, Air Blowing Nipples)
|
| Grade/Plasticizer Content(PHR) |
SO-30X |
| A |
B |
C |
D |
E |
F |
| Items / Test Method (ASTM) |
50 |
60 |
70 |
80 |
90 |
100 |
| Specific Gravity |
D-792 |
1.25 |
1.23 |
1.22 |
1.22 |
1.21 |
1.20 |
| Hardness (shore A) |
D-2240 |
85 |
80 |
76 |
66 |
63 |
56 |
| Tensile Strength (kg/cm2) |
D-638 |
270 |
210 |
200 |
110 |
80 |
68 |
| Elongation (%) |
D-638 |
190 |
165 |
156 |
145 |
110 |
80 |
| 100% Modulus (kg/cm2) |
D-638 |
110 |
80 |
70 |
60 |
50 |
40 |
| Tearing Strength (kg/cm) |
D-638 |
65 |
55 |
50 |
45 |
40 |
30 |
| Heating Volatility (%) |
D-1203 |
0.3 |
0.3 |
0.3 |
0.4 |
0.4 |
0.5 |
|
|
RIGID TYPE COMPOUNDS Physical Properties
General Extrusion, Injection Products
|
| Grade |
R-11X |
| Extrusion |
Injection |
| Items / Test Method (ASTM) |
NI |
MI |
HI |
NI |
MI |
HI |
| Specific Gravity |
D-792 |
1.38 |
1.37 |
1.36 |
1.36 |
1.35 |
1.34 |
| Tensile Strength (kg/cm2) |
D-638 |
545 |
540 |
520 |
550 |
540 |
430 |
| Elongation (%) |
D-638 |
55 |
50 |
40 |
60 |
50 |
45 |
| Impact Strength (kg-cm/cm2) |
D-256 |
6 |
8 |
14 |
5 |
8 |
10 |
| Vicat Softening Point (℃) |
D-1525 |
92 |
91 |
90 |
92 |
91 |
90 |
|
Food Vessels And Containers , Packing Bar
For Electronic Components , Heat Shrinkable
|
| Grade |
R-10X |
| Bottle Blowing |
Extrusion |
| Items / Test Method (ASTM) |
NI |
MI |
HI |
NI |
MI |
HI |
| Specific Gravity |
D-792 |
Pellet 1.345 |
Pellet 1.35 |
Pellet 1.34 |
1.37 |
1.38 |
1.37 |
| Tensile Strength (kg/cm2) |
D-638 |
500 |
480 |
460 |
610 |
620 |
540 |
| Elongation (%) |
D-638 |
70 |
90 |
110 |
60 |
88 |
90 |
| Impact Strength (kg-cm/cm2) |
D-256 |
6 |
12 |
20 |
2 |
2.4 |
2.4 |
| Vicat Softening Point (℃) |
D-1525 |
86 |
84 |
82 |
90 |
91 |
91 |
|
|
Top